Aim and Objectives:This research work deals with the highly selective oxidation of benzyl alcohol to benzaldehyde by palladium doped graphene oxide catalyst, which was synthesized by a modified Hummer’s method. The effect of reaction parameters like temperature, time and catalyst loading were studied. It was found that fine-tuning of reaction temperature and presence of a small amount of benzyl alcohol in a product prevented the undesirable formation of benzoic acid crystals, which form on auto-oxidation of benzaldehyde. Benzoic acid or substituted benzoic acid formation was hindered by the presence of < 2% benzyl alcohol at a reaction temperature of 50˚C, which was further supported by palladium doped graphene oxide catalyst. Materials and Methods: Modified Hummer’s method was used for the synthesis of graphene oxide and palladium doped graphene oxide was synthesized by in-situ method in which graphene oxide dispersed in 20mL of distilled water was ultrasonicated for 2h. Palladium solution was added and it was further ultrasonicated for 30min for homogeneous deposition of palladium on a graphene oxide support. To this, 2 mL of sodium borohydride solution was added and stirred at room temperature for 4h. The resulting solution was centrifuged, and the residue was dried at 60°C for 12 h. Results: The morphological characteristics and the functional groups of supported catalysts were characterized by X-ray diffraction, Field emission scanning spectroscopy, and Fourier transform infrared spectroscopy. The produced benzaldehyde was characterized by gas chromatography. Conclusion: PdGO catalyst was prepared using sodium borohydride as a reducing agent by modified Hummer’s method and utilized for the oxidation of benzyl alcohol to benzaldehyde. A maximum conversion of 89% and selectivity of 99% were obtained and the catalyst could be reused up to five times without any compromise on conversion and selectivity.

Loading

Article metrics loading...

/content/journals/cchts/10.2174/1386207323666201230091613
2022-02-01
2025-02-19
Loading full text...

Full text loading...

/content/journals/cchts/10.2174/1386207323666201230091613
Loading
This is a required field
Please enter a valid email address
Approval was a Success
Invalid data
An Error Occurred
Approval was partially successful, following selected items could not be processed due to error
Please enter a valid_number test